Compressive strength of hybrid composites resin with post curing light emitting diode using three different sizes of lightbox

Author :

  1. Mirza Aryanto*1
  2. Milly Armilia*2
  3. Dudi Aripin*3
  1. Bagian Konservasi Gigi, Fakultas Kedokteran Gigi Universitas Prof. Dr. Moestopo (B), Jakarta – Indonesia
  2. Bagian Konservasi Gigi, Fakultas Kedokteran Gigi Universitas Padjadjaran, Bandung – Indonesia
  3. Bagian Konservasi Gigi, Fakultas Kedokteran Gigi Universitas Padjadjaran, Bandung – Indonesia

Abstract :

Background: Post-curing methods can be used to increase strength to the composite resin. Purpose: To determine the difference of compressive strength of post cured hybrid composite resin by using three different size of lightbox. Methods: This research was conducted in a true in vitro experiment. Research carried out by making a tube-shaped cylinder hybrid with 3 mm diameter and 6 mm  height composite resin samples post cured by using 3 different size of light box, 3 cm x 3 cm x 3 cm (A), 4 cm x 4 cm x 4 cm (B) 6 cm x 6 cm x 6 cm (C), and a non post-curing control. Compressive strength test was then performed using a universal testing machine. Each sample was tested and averaged to obtain values in order to be analyzed statistically using ANOVA and multiple comparison. Results: There is an increase in compressive strength of each group, namely group A (172.9460 MPa), B (154.821 MPa), C (154.0789 MPa) and control (123.3550 MPa), and a statistically significant difference (F<0.05). Conclusion: The smaller size of the lightbox is used, the higher the compressive strength of composite resin.

Keyword :

compressive strength, post curing, lightbox, hybrid composite resin,


References :

Roberson TM,(2006) Sturdevant’s art and science of operative dentistry St. Louis : Mosby Inc





Archive Article

Cover Media Content

Volume : 46 / No. : 2 / Pub. : 2013-06
  1. Enamel Defect Of Primary Dentition In Sga Children In Relation To Onset Time Of Intrauterine Growth Disturbance
  2. Description Of Pulp Chamber Density In Deciduous Teeth Using Cone Beam Ct-3d
  3. A Study Of Extraction And Characterization Of Alginates Obtained From Brown Macroalgae Sargassum Duplicatum And Sargassum Crassifolium From Indonesia
  4. Effectiveness Of Various Sterilization Methods Of Contaminated Post-fitted Molar Band
  5. Peroxide Alkaline For Cleansing The Baby Bottle Nipple To Prevent Oral Thrush Relaps
  6. Treatment Of Non-vital Primary Molar Using Lesion Sterilization And Tissue Repair (lstr 3mix-mp)
  7. New Concept In Allergy: Non-allergic Rats Becomes Allergic After Induced By Porphyromonas Gingivalis Lipopolysaccharide
  8. Ricketts Esthetic Line At Student Of Faculty Of Dentistry Universitas Airlangga
  9. Dental Student’s Perception To Aesthetic Component Of Iotn And Demand For Orthodontic Treatment
  10. Compressive Strength Of Hybrid Composites Resin With Post Curing Light Emitting Diode Using Three Different Sizes Of Lightbox
  11. Bitemark Identification With Chelex Methods In Dna Extraction

Information DENTJ