The change of temperature on the shear strength of permanent soft-liner on acrylic resin

Author :

  1. Waloejo Noegroho*1
  2. Utari Kresnoadi*2
  3. Adi Subianto*3
  1. Staff of Bhayangkara Hospital, Polda Jatim
  2. Department of Prostodontic, Faculty of Dentistry Airlangga University Surabaya – Indonesia
  3. (2) Department of Prostodontic, Faculty of Dentistry Airlangga University Surabaya – Indonesia

Abstract :

The characteristics of dental material such as solubility and water resorption, the use of adhesive, storage condition or used as thermo cycling or elevated-temperature are factors that can effect bond strength. The purpose of this study was to investigate the change of temperature on the shear strength of permanent soft liner on acrylic resin. Twenty-four specimens were divided into 3 groups and immersed in water at: 5 °C, 37 °C and 55 °C. Autograph AG 10 TE Shimadzu was used to determine the shear strength. The statistical test (ANOVA and LSD); showed that there were significant differences between temperature groups. The shear strength of 37 °C was higher than the temperature of 5 °C and 55 °C.

Keyword :

temperature, shear strength, permanent soft liner, acrylic resin ,


References :

Huggett,(1990) Soft lining materials in prosthetic dentistry: A Review - : Journal Prosthetic Dentistry

Anusavice,(2004) Phillip’s ilmu bahan kedokteran gigi Jakarta : EGC Publisher

Hadary,(2000) Comparative study of water sorption, solubility, and tensile bond strength of soft lining material - : Journal Prosthetic Dentistry

Drummond,(2000) Comparative study of water sorption, solubility, and tensile bond strength of soft lining material - : Journal Prosthetic Dentistry

Baysan,(1998) Adhesion and tear energy of a long-term soft lining material activated by rapid microwave energy - : Journal Prosthetic Dentistry

Parker,(1998) Adhesion and tear energy of a long-term soft lining material activated by rapid microwave energy - : Journal Prosthetic Dentistry

Wright,(1998) Adhesion and tear energy of a long-term soft lining material activated by rapid microwave energy - : Journal Prosthetic Dentistry

Hamada,(2003)



Archive Article

Cover Media Content

Volume : 39 / No. : 2 / Pub. : 2006-06
  1. The Density Of Collagen Fiber In Alveolus Mandibular Bone Of Rabbit After Augmentation With Powder Demineralized Bone Matrix Post Incisivus Extraction
  2. Placement Of Replace Select Ti-unite-coated Type Implants Using A Combination Of Immediate And Submerge Techniques After Tooth Extraction
  3. Nursing Habits And Early Childhood Caries In Children Attending Hospital University Science Malaysia (husm)
  4. Tensile Bond Strength Of Hydroxyethyl Methacrylate (hema) Bonding Agent To Bovine Dentine Surface At Various Humidity
  5. Sensitization Of The Sphenopalatine Ganglion (spg) By Periodontal Inflammation: A Possible Etiology Of Sinusitis And Headache In Children
  6. Oral And Dental Aspects Of Child Abuse
  7. The Business Of Dental Practice
  8. The Change Of Temperature On The Shear Strength Of Permanent Soft-liner On Acrylic Resin
  9. Candidosis On Oral Lichen Planus
  10. Surface Hardness Of Hybrid Ionomer Cement After Immersion In Antiseptic Solution

Information DENTJ